Type | TS-70A | TS-70C | |
---|---|---|---|
Aldary | material | ZQAL9-4 | ZQAL9-4 |
hardness | ≥110HB | ≥110HB | |
intensity of tension | ≥390Mpa | ≥390Mpa | |
plastics | Reinforcing polytetrafluoroethylene | Oil nylon plastic alloy | |
rail radius ( mm ) | 150 300 | 150 300 | |
allowableload ( KN/mm ) | 3 5 | 4 7 | |
friction coefficient | ageingμ∞ | ≤0.1 | ≤0.1 |
stillness (water)μo | 0.075 | 0.080 | |
dynamic(min)μd | 0.055 | 0.055 | |
slideway allow wearing capacity ( mm ) | 2.5 | 2.5 | |
allow wearing stroke ( m ) | 2500 | 4000 | |
In force wearing stroke ( mm ) | 4 | 4 | |
Standard Dimension | Total thickness( mm ) | 20±0.1 | |
Length ( mm ) | 2500-0.5 3000-0.5 3500-0.5 4000-0.5 5000-0.5 | ||
Width ( mm ) | 120±0.3 160±0.3 | ||
NSP Nonstandard Part | According to the original processing | ||
Appearance | Copper alloy without cracks, allowing a small amount of plastic pore |